Poly(delta-gluconolactone) and Poly(delta-gluconolactone-ε-caprolactone) from delta-Gluconolactone and ε-Caprolactone by Ring-Opening Polymerization
Poly(delta-gluconolactone) (PGL) and poly(delta-gluconolactone-ε-caprolactone) (P(GL-CL)) were synthesized through ring-opening polymerization (ROP) and characterized by FT-IR, NMR, XRD, intrinsic viscosity, GPC, DSC, and TGA. The crystallinity of P(GL-CL) with various d-GL/CL ratios (d-GL/CL = 5 : ...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2018-01-01
|
| Series: | International Journal of Polymer Science |
| Online Access: | http://dx.doi.org/10.1155/2018/5381582 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Poly(delta-gluconolactone) (PGL) and poly(delta-gluconolactone-ε-caprolactone) (P(GL-CL)) were synthesized through ring-opening polymerization (ROP) and characterized by FT-IR, NMR, XRD, intrinsic viscosity, GPC, DSC, and TGA. The crystallinity of P(GL-CL) with various d-GL/CL ratios (d-GL/CL = 5 : 5, 4 : 6, 3 : 7, 2 : 8, and 1 : 9) was 12.09 to 59.78% while PGL was amorphous. Melting temperature (Tm) of these polymers was 49.8 to 62.0°C and decomposition temperature was 282 to 489°C depending on the d-GL/CL ratios. In addition, all these polymers were degradable and the degradation rates could be controlled by adjusting d-GL/CL ratios. These results indicated that PGL and P(GL-CL) might be promising novel absorbable materials. |
|---|---|
| ISSN: | 1687-9422 1687-9430 |