Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging
The first damage mechanism in composites in tension is transverse cracking, which is here studied in 3D at a kHz rate, using time-resolved X-ray multi-projection imaging. Radiographs taken at three angles with synchrotron radiation enabled the detection of crack propagation and other damage mechan...
Saved in:
| Main Authors: | , , , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | deu |
| Published: |
NDT.net
2025-02-01
|
| Series: | e-Journal of Nondestructive Testing |
| Online Access: | https://www.ndt.net/search/docs.php3?id=30757 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832086604833882112 |
|---|---|
| author | Elise Van Vlierberghe Jeroen Soete Eleni Myrto Asimakopoulou Zisheng Yao Julia Rogalinski Zhe Hu Kannara Mom Bratislav Lukić Christian Breite Pablo Villanueava Perez Yentl Swolfs |
| author_facet | Elise Van Vlierberghe Jeroen Soete Eleni Myrto Asimakopoulou Zisheng Yao Julia Rogalinski Zhe Hu Kannara Mom Bratislav Lukić Christian Breite Pablo Villanueava Perez Yentl Swolfs |
| author_sort | Elise Van Vlierberghe |
| collection | DOAJ |
| description |
The first damage mechanism in composites in tension is transverse cracking, which is here studied in 3D at a kHz rate, using time-resolved X-ray multi-projection imaging. Radiographs taken at three angles with synchrotron radiation enabled the detection of crack propagation and other damage mechanisms related to the final failure of composites. Deep learning segmentation has been proven effective in analysing the crack shape before a crack opening occurs. With these tools, a comparison between different lay-ups revealed that external transverse plies are much weaker than internal ones. An extensive data set was gathered to make a 3D reconstruction of the crack evolution over time using XMPI and machine learning-based reconstruction algorithms.
|
| format | Article |
| id | doaj-art-e52b81a94cc9460b865b9fbfb85f4d6f |
| institution | Kabale University |
| issn | 1435-4934 |
| language | deu |
| publishDate | 2025-02-01 |
| publisher | NDT.net |
| record_format | Article |
| series | e-Journal of Nondestructive Testing |
| spelling | doaj-art-e52b81a94cc9460b865b9fbfb85f4d6f2025-02-06T10:48:19ZdeuNDT.nete-Journal of Nondestructive Testing1435-49342025-02-0130210.58286/30757Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imagingElise Van VlierbergheJeroen SoeteEleni Myrto AsimakopoulouZisheng YaoJulia RogalinskiZhe HuKannara MomBratislav LukićChristian BreitePablo Villanueava PerezYentl Swolfs The first damage mechanism in composites in tension is transverse cracking, which is here studied in 3D at a kHz rate, using time-resolved X-ray multi-projection imaging. Radiographs taken at three angles with synchrotron radiation enabled the detection of crack propagation and other damage mechanisms related to the final failure of composites. Deep learning segmentation has been proven effective in analysing the crack shape before a crack opening occurs. With these tools, a comparison between different lay-ups revealed that external transverse plies are much weaker than internal ones. An extensive data set was gathered to make a 3D reconstruction of the crack evolution over time using XMPI and machine learning-based reconstruction algorithms. https://www.ndt.net/search/docs.php3?id=30757 |
| spellingShingle | Elise Van Vlierberghe Jeroen Soete Eleni Myrto Asimakopoulou Zisheng Yao Julia Rogalinski Zhe Hu Kannara Mom Bratislav Lukić Christian Breite Pablo Villanueava Perez Yentl Swolfs Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging e-Journal of Nondestructive Testing |
| title | Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging |
| title_full | Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging |
| title_fullStr | Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging |
| title_full_unstemmed | Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging |
| title_short | Transverse cracking in glass fibre-reinforced composites monitored with synchrotron X-ray multi-projection imaging |
| title_sort | transverse cracking in glass fibre reinforced composites monitored with synchrotron x ray multi projection imaging |
| url | https://www.ndt.net/search/docs.php3?id=30757 |
| work_keys_str_mv | AT elisevanvlierberghe transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT jeroensoete transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT elenimyrtoasimakopoulou transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT zishengyao transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT juliarogalinski transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT zhehu transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT kannaramom transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT bratislavlukic transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT christianbreite transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT pablovillanueavaperez transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging AT yentlswolfs transversecrackinginglassfibrereinforcedcompositesmonitoredwithsynchrotronxraymultiprojectionimaging |