Sustainable composites from microcrystalline cellulose and cellulose acetate: 3D printing and performance optimization
Novel green composites were developed using microcrystalline cellulose (MCC) and plasticized cellulose acetate (pCA) to assess their viability for application in additive manufacturing (AM), specifically fused filament fabrication (FFF). This study represents one of the first attempts to fabricate a...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2025-07-01
|
| Series: | Composites Part C: Open Access |
| Subjects: | |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S2666682025000490 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Novel green composites were developed using microcrystalline cellulose (MCC) and plasticized cellulose acetate (pCA) to assess their viability for application in additive manufacturing (AM), specifically fused filament fabrication (FFF). This study represents one of the first attempts to fabricate and optimize a sustainable MCC-pCA composite for use as a 3D printing filament. The Taguchi L27 experimental design was employed to optimize five critical FFF parameters, namely nozzle temperature, printing speed, infill density, raster angle, and layer height, with the objective of maximizing mechanical performance. Optimal printing parameters were determined to be a nozzle temperature of 230 °C, a printing speed of 1800 mm/min, an infill density of 100 %, a raster angle of 0°, and a layer height of 0.15 mm. Under these conditions, the 3D-printed samples exhibited mechanical properties comparable to those of injection-molded counterparts, with a 37 % increase in impact strength. The coefficient of linear thermal expansion (CLTE) of the optimized 3D-printed sample was 89.36 μm/m °C (perpendicular) and 65.39 μm/m °C (parallel), demonstrating lower thermal expansion than injection-molded counterparts (108.65 μm/m °C and 47.06 μm/m °C, respectively). Furthermore, the heat deflection temperature (HDT) of the optimized 3D-printed sample was 92.18 °C, surpassing that of injection-molded samples (69.59 °C), indicating superior thermal resistance in the 3D-printed part. As a proof-of-concept, a 3D printed finger splint was fabricated using the optimized parameters, showcasing the potential of this sustainable composite for biomedical applications. |
|---|---|
| ISSN: | 2666-6820 |