Excellent high-temperature strength of (HfZrTiTaNb)C high-entropy carbide diffusion-bonded joint via in-situ alloying of Ni/Nb/Ni composite interlayer
To obtain high-entropy carbide (HEC) joints with excellent high-temperature performance, a (HfZrTiTaNb)C HEC joint featuring a direct diffusion-bonded interface with a Nb-based interlayer was successfully fabricated at relatively low temperatures of 1150–1250 °C for 60 min under 10 MPa. Starting fro...