Fracture Characteristics of Polyurethane Grouting Materials Based on Acoustic Emission Monitoring
In this study, 16 groups of tests were designed by the orthogonal test method, and a PU grouting material was prepared, which can be used for the construction of sealing wall in mined-out area of coal mine. The basic properties of the material were measured. Firstly, the viscosity of four groups of...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2021-01-01
|
| Series: | Shock and Vibration |
| Online Access: | http://dx.doi.org/10.1155/2021/8888691 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In this study, 16 groups of tests were designed by the orthogonal test method, and a PU grouting material was prepared, which can be used for the construction of sealing wall in mined-out area of coal mine. The basic properties of the material were measured. Firstly, the viscosity of four groups of samples with different polyether polyol contents was measured by a dynamic rheometer. Secondly, the uniaxial compressive strength of pure slurry samples and sand-containing samples was measured by a universal testing machine. Finally, the failure process of sand-containing samples was monitored by acoustic emission equipment. Through the above research and analysis, a PU grouting material with excellent performance has been obtained. That is, when the ratio of polyether triol:polyether tetraol:catalyst:surfactant:chain extender:plasticizer is 11 : 9 : 0.5 : 1.0 : 1.2 : 6.0, PU grouting material has higher injectability and ideal compressive strength, which has been proved in grouting experiments. |
|---|---|
| ISSN: | 1070-9622 1875-9203 |