Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner
Back ground: Reduction of a durable bond to acrylic denture base is the main problem associated with soft liner materials. Purpose: Evaluation of the influence of addition of Ag-Zn Zeolite on shear bond strength of silicon cold cure soft liner. Approach: thirty specimens of silicon cold c...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
middle technical university
2021-03-01
|
| Series: | Journal of Techniques |
| Subjects: | |
| Online Access: | https://journal.mtu.edu.iq/index.php/MTU/article/view/270 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832595087643639808 |
|---|---|
| author | Huda Alaa Aldeen Sadeq Israa Mohammed Hummudi |
| author_facet | Huda Alaa Aldeen Sadeq Israa Mohammed Hummudi |
| author_sort | Huda Alaa Aldeen Sadeq |
| collection | DOAJ |
| description |
Back ground: Reduction of a durable bond to acrylic denture base is the main problem associated with soft liner materials.
Purpose: Evaluation of the influence of addition of Ag-Zn Zeolite on shear bond strength of silicon cold cure soft liner.
Approach: thirty specimens of silicon cold cure soft liner were constructed for shear bond- strength test and divided into three groups: Control groups: 10 specimens without incorporation of Ag-Zn Zeolite, Experimental group: 10 specimens with 0.5% by weight of Ag-Zn Zeolite Experimental Group: 10 specimens with 0.75 %by weight of Ag-Zn Zeolite Plastic pattern of acrylic block with dimensions (75 mm length x 25mm width x 5mm depth )was fabricated and evaluated by Instron testing machine.
Results: Least significant difference of (0.75%) of Ag-Zn zeolite group was significantly different compared with the experimental group of (0.5% and control group) at p<0.05.
Conclusion: The incorporation of 0.5%, 0.75% by weight into silicon cold cure soft liner had significant effect and causes improvement in shear bond strength.
|
| format | Article |
| id | doaj-art-fe0aaed6b49c4d1b8ea74c83800191c5 |
| institution | Kabale University |
| issn | 1818-653X 2708-8383 |
| language | English |
| publishDate | 2021-03-01 |
| publisher | middle technical university |
| record_format | Article |
| series | Journal of Techniques |
| spelling | doaj-art-fe0aaed6b49c4d1b8ea74c83800191c52025-01-19T11:09:04Zengmiddle technical universityJournal of Techniques1818-653X2708-83832021-03-013110.51173/jt.v3i1.270Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft LinerHuda Alaa Aldeen Sadeq0Israa Mohammed Hummudi1Minstry of Iraqi health, Baghdad.Middle Technical university- College of Health and Medical Technologies- Baghdad-Iraq Back ground: Reduction of a durable bond to acrylic denture base is the main problem associated with soft liner materials. Purpose: Evaluation of the influence of addition of Ag-Zn Zeolite on shear bond strength of silicon cold cure soft liner. Approach: thirty specimens of silicon cold cure soft liner were constructed for shear bond- strength test and divided into three groups: Control groups: 10 specimens without incorporation of Ag-Zn Zeolite, Experimental group: 10 specimens with 0.5% by weight of Ag-Zn Zeolite Experimental Group: 10 specimens with 0.75 %by weight of Ag-Zn Zeolite Plastic pattern of acrylic block with dimensions (75 mm length x 25mm width x 5mm depth )was fabricated and evaluated by Instron testing machine. Results: Least significant difference of (0.75%) of Ag-Zn zeolite group was significantly different compared with the experimental group of (0.5% and control group) at p<0.05. Conclusion: The incorporation of 0.5%, 0.75% by weight into silicon cold cure soft liner had significant effect and causes improvement in shear bond strength. https://journal.mtu.edu.iq/index.php/MTU/article/view/270SilverZincZeoliteShear bondsilicon |
| spellingShingle | Huda Alaa Aldeen Sadeq Israa Mohammed Hummudi Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner Journal of Techniques Silver Zinc Zeolite Shear bond silicon |
| title | Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner |
| title_full | Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner |
| title_fullStr | Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner |
| title_full_unstemmed | Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner |
| title_short | Influence of Silver-Zinc Zeolite Incorporation on Shear Bond Strength of Silicon Cold Cure Soft Liner |
| title_sort | influence of silver zinc zeolite incorporation on shear bond strength of silicon cold cure soft liner |
| topic | Silver Zinc Zeolite Shear bond silicon |
| url | https://journal.mtu.edu.iq/index.php/MTU/article/view/270 |
| work_keys_str_mv | AT hudaalaaaldeensadeq influenceofsilverzinczeoliteincorporationonshearbondstrengthofsiliconcoldcuresoftliner AT israamohammedhummudi influenceofsilverzinczeoliteincorporationonshearbondstrengthofsiliconcoldcuresoftliner |