The effect of zirconium on the strength cold-deformed reinforcement properties
The possibility of using zirconium in the steel composition of the Arx-Zr brand in the cold-deformed reinforcement of a threesided periodic profile of strength class 500 MPa manufacture in order to increase the finished reinforcement strength characteristics is determined. There is test results info...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Belarusian National Technical University
2022-03-01
|
| Series: | Литьë и металлургия |
| Subjects: | |
| Online Access: | https://lim.bntu.by/jour/article/view/3420 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832543249158373376 |
|---|---|
| author | E. S. Eltsova O. Yu. Khodosovskaya Yu. I. Kozyreva |
| author_facet | E. S. Eltsova O. Yu. Khodosovskaya Yu. I. Kozyreva |
| author_sort | E. S. Eltsova |
| collection | DOAJ |
| description | The possibility of using zirconium in the steel composition of the Arx-Zr brand in the cold-deformed reinforcement of a threesided periodic profile of strength class 500 MPa manufacture in order to increase the finished reinforcement strength characteristics is determined. There is test results information of a wire rod /blank with an 8.8 mm diameter, which is intended for the manufacture of cold-deformed fittings with an 8.0 mm diameter, are presented. A comparative analysis of the physical and mechanical finished cold-deformed fittings properties with an 8.0 mm diameter made of steel grade Arch-Zr and fittings of a three-sided periodic profile made of wire rod of ordinary quality was done. Analyzed the obtained properties and the cold-deformed fittings evaluation for meeting the standards’ requirements. Identified that the addition of zirconium to steel in an amount of 0.019 % does not affect the final strength characteristics of the produced cold-deformed reinforcement of a three-sided periodic profile of strength class 500 MPa. The values of the physical and mechanical parameters of the produced cold-deformed reinforcement are similar to the cold-formed reinforcement parameters made of wire rod of ordinary quality without the use of alloying. |
| format | Article |
| id | doaj-art-f4cc785f4b9545a9bad833813393da6f |
| institution | Kabale University |
| issn | 1683-6065 2414-0406 |
| language | English |
| publishDate | 2022-03-01 |
| publisher | Belarusian National Technical University |
| record_format | Article |
| series | Литьë и металлургия |
| spelling | doaj-art-f4cc785f4b9545a9bad833813393da6f2025-02-03T11:51:16ZengBelarusian National Technical UniversityЛитьë и металлургия1683-60652414-04062022-03-0101616310.21122/1683-6065-2022-1-61-633301The effect of zirconium on the strength cold-deformed reinforcement propertiesE. S. Eltsova0O. Yu. Khodosovskaya1Yu. I. Kozyreva2BSW – Management Company of the Holding «BMC»BSW – Management Company of the Holding «BMC»BSW – Management Company of the Holding «BMC»The possibility of using zirconium in the steel composition of the Arx-Zr brand in the cold-deformed reinforcement of a threesided periodic profile of strength class 500 MPa manufacture in order to increase the finished reinforcement strength characteristics is determined. There is test results information of a wire rod /blank with an 8.8 mm diameter, which is intended for the manufacture of cold-deformed fittings with an 8.0 mm diameter, are presented. A comparative analysis of the physical and mechanical finished cold-deformed fittings properties with an 8.0 mm diameter made of steel grade Arch-Zr and fittings of a three-sided periodic profile made of wire rod of ordinary quality was done. Analyzed the obtained properties and the cold-deformed fittings evaluation for meeting the standards’ requirements. Identified that the addition of zirconium to steel in an amount of 0.019 % does not affect the final strength characteristics of the produced cold-deformed reinforcement of a three-sided periodic profile of strength class 500 MPa. The values of the physical and mechanical parameters of the produced cold-deformed reinforcement are similar to the cold-formed reinforcement parameters made of wire rod of ordinary quality without the use of alloying.https://lim.bntu.by/jour/article/view/3420cold-deformed reinforcementsteelthree-sided periodic profilestrength class 500 mpazirconiumstrength characteristics |
| spellingShingle | E. S. Eltsova O. Yu. Khodosovskaya Yu. I. Kozyreva The effect of zirconium on the strength cold-deformed reinforcement properties Литьë и металлургия cold-deformed reinforcement steel three-sided periodic profile strength class 500 mpa zirconium strength characteristics |
| title | The effect of zirconium on the strength cold-deformed reinforcement properties |
| title_full | The effect of zirconium on the strength cold-deformed reinforcement properties |
| title_fullStr | The effect of zirconium on the strength cold-deformed reinforcement properties |
| title_full_unstemmed | The effect of zirconium on the strength cold-deformed reinforcement properties |
| title_short | The effect of zirconium on the strength cold-deformed reinforcement properties |
| title_sort | effect of zirconium on the strength cold deformed reinforcement properties |
| topic | cold-deformed reinforcement steel three-sided periodic profile strength class 500 mpa zirconium strength characteristics |
| url | https://lim.bntu.by/jour/article/view/3420 |
| work_keys_str_mv | AT eseltsova theeffectofzirconiumonthestrengthcolddeformedreinforcementproperties AT oyukhodosovskaya theeffectofzirconiumonthestrengthcolddeformedreinforcementproperties AT yuikozyreva theeffectofzirconiumonthestrengthcolddeformedreinforcementproperties AT eseltsova effectofzirconiumonthestrengthcolddeformedreinforcementproperties AT oyukhodosovskaya effectofzirconiumonthestrengthcolddeformedreinforcementproperties AT yuikozyreva effectofzirconiumonthestrengthcolddeformedreinforcementproperties |