Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints
The objective of this study was to determine adhesive strength of particleboard and medium density fiberboard (MDF) finished with two types of paints. Samples were coated using cellulosic and polyurethane based paints. Adhesion strength and coating layer thickness of each sample were measured using...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2015-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2015/745675 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832545752670273536 |
|---|---|
| author | Tuncer Dilik Seda Erdinler Ender Hazır Hüseyin Koç Salim Hiziroglu |
| author_facet | Tuncer Dilik Seda Erdinler Ender Hazır Hüseyin Koç Salim Hiziroglu |
| author_sort | Tuncer Dilik |
| collection | DOAJ |
| description | The objective of this study was to determine adhesive strength of particleboard and medium density fiberboard (MDF) finished with two types of paints. Samples were coated using cellulosic and polyurethane based paints. Adhesion strength and coating layer thickness of each sample were measured using pull-off testing method and PosiTector equipment, respectively. The highest adhesion strength value of 3.62 MPa was found for MDF samples coated with paint. Based on the statistical analysis type of substrate significantly influenced overall adhesion strength of the samples while type and layer thickness of paint as well as number of layers applied to the surface of specimens have not affected significantly adhesion resistance of the panels used in this work. It appears that pull-off test can effectively be used to determine and evaluate adhesion strength of the samples considered in the experiments. |
| format | Article |
| id | doaj-art-f3e23e7cfbc844478cdfd9337e418e06 |
| institution | Kabale University |
| issn | 1687-8434 1687-8442 |
| language | English |
| publishDate | 2015-01-01 |
| publisher | Wiley |
| record_format | Article |
| series | Advances in Materials Science and Engineering |
| spelling | doaj-art-f3e23e7cfbc844478cdfd9337e418e062025-02-03T07:24:49ZengWileyAdvances in Materials Science and Engineering1687-84341687-84422015-01-01201510.1155/2015/745675745675Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane PaintsTuncer Dilik0Seda Erdinler1Ender Hazır2Hüseyin Koç3Salim Hiziroglu4Department of Forest Industrial Engineering, Faculty of Forestry, Istanbul University, 34473 Istanbul, TurkeyDepartment of Forest Industrial Engineering, Faculty of Forestry, Istanbul University, 34473 Istanbul, TurkeyDepartment of Forest Industrial Engineering, Faculty of Forestry, Istanbul University, 34473 Istanbul, TurkeyDepartment of Forest Industrial Engineering, Faculty of Forestry, Istanbul University, 34473 Istanbul, TurkeyNatural Resource Ecology and Management, Oklahoma State University, Stillwater, OK 74078-6013, USAThe objective of this study was to determine adhesive strength of particleboard and medium density fiberboard (MDF) finished with two types of paints. Samples were coated using cellulosic and polyurethane based paints. Adhesion strength and coating layer thickness of each sample were measured using pull-off testing method and PosiTector equipment, respectively. The highest adhesion strength value of 3.62 MPa was found for MDF samples coated with paint. Based on the statistical analysis type of substrate significantly influenced overall adhesion strength of the samples while type and layer thickness of paint as well as number of layers applied to the surface of specimens have not affected significantly adhesion resistance of the panels used in this work. It appears that pull-off test can effectively be used to determine and evaluate adhesion strength of the samples considered in the experiments.http://dx.doi.org/10.1155/2015/745675 |
| spellingShingle | Tuncer Dilik Seda Erdinler Ender Hazır Hüseyin Koç Salim Hiziroglu Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints Advances in Materials Science and Engineering |
| title | Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints |
| title_full | Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints |
| title_fullStr | Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints |
| title_full_unstemmed | Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints |
| title_short | Adhesion Strength of Wood Based Composites Coated with Cellulosic and Polyurethane Paints |
| title_sort | adhesion strength of wood based composites coated with cellulosic and polyurethane paints |
| url | http://dx.doi.org/10.1155/2015/745675 |
| work_keys_str_mv | AT tuncerdilik adhesionstrengthofwoodbasedcompositescoatedwithcellulosicandpolyurethanepaints AT sedaerdinler adhesionstrengthofwoodbasedcompositescoatedwithcellulosicandpolyurethanepaints AT enderhazır adhesionstrengthofwoodbasedcompositescoatedwithcellulosicandpolyurethanepaints AT huseyinkoc adhesionstrengthofwoodbasedcompositescoatedwithcellulosicandpolyurethanepaints AT salimhiziroglu adhesionstrengthofwoodbasedcompositescoatedwithcellulosicandpolyurethanepaints |