Effect of Internal Curing with Superabsorbent Polymers on Bond Behavior of High-Strength Concrete
High-strength concrete (HSC) is widely used in engineering due to its high strength and durability. However, because of its low water-to-cement ratio, external curing water hardly enters the dense internal structure of HSC so that high self-desiccation shrinkage often takes place. As a result, super...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2020-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2020/6651452 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | High-strength concrete (HSC) is widely used in engineering due to its high strength and durability. However, because of its low water-to-cement ratio, external curing water hardly enters the dense internal structure of HSC so that high self-desiccation shrinkage often takes place. As a result, superabsorbent polymers (SAP) are added as an internal curing material to effectively reduce the shrinkage of high-performance concrete. Meanwhile, the bond performance between reinforcing steel and SAP HSC concrete remains unknown. In this paper, the bond performance of HSC mixed with SAP is studied by pull-out tests, and the results were obtained as follows: (1) the bond strength of HSC mixed with SAP increased first and then decreased with the increase of SAP content; (2) the slip at ultimate bond strength of HSC with SAP decreased with the increase of compressive strength; (3) a prediction model of the stress-slip relationship between steel rebars and HSC was established. |
|---|---|
| ISSN: | 1687-8434 1687-8442 |