Characterization, Dissolution, and Solubility of Zn-Substituted Hydroxylapatites [(ZnxCa1−x)5(PO4)3OH] at 25°C
A series of Zn-substituted hydroxylapatites [(ZnxCa1−x)5(PO4)3OH, Zn-Ca-HA] with the Zn/(Zn + Ca) molar ratio (XZn) of 0~0.16 was prepared and characterized, and then the dissolution of the synthesized solids in aqueous solution was investigated by batch experiment. The results indicated that the aq...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2017-01-01
|
| Series: | Journal of Chemistry |
| Online Access: | http://dx.doi.org/10.1155/2017/4619159 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A series of Zn-substituted hydroxylapatites [(ZnxCa1−x)5(PO4)3OH, Zn-Ca-HA] with the Zn/(Zn + Ca) molar ratio (XZn) of 0~0.16 was prepared and characterized, and then the dissolution of the synthesized solids in aqueous solution was investigated by batch experiment. The results indicated that the aqueous zinc, calcium, and phosphate concentrations greatly depended on the Zn/(Zn + Ca) molar ratio of the Zn-Ca-HA solids (XZn). For the Zn-Ca-HA dissolution at 25°C with an initial pH of 2.00, the final solution pH increased, while the final solution calcium and phosphate concentrations decreased with the increasing XZn. The final solution zinc concentrations increased with the increasing XZn when XZn≤0.08 and decreased with the increasing XZn when XZn = 0.08~0.16. The mean Ksp values for (ZnxCa1−x)5(PO4)3OH at 25°C decreased from 10−57.75 to 10−58.59 with the increasing XZn from 0.00 to 0.08 and then increased from 10–58.59 to 10–56.63 with the increasing XZn from 0.08 to 0.16. This tendency was consistent with the dependency of the lattice parameter a on XZn. The corresponding free energies of formation (ΔGfo) increased lineally from −6310.45 kJ/mol to −5979.39 kJ/mol with the increasing XZn from 0.00 to 0.16. |
|---|---|
| ISSN: | 2090-9063 2090-9071 |