The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior

This paper investigated the wear performances of Y2O3 doped MA6000 (Ni-Cr-Al) alloy produced by mechanical alloying (MA). Produced, all powders were pre-formed by cold pressing and sintered in a vacuum environment. Sintered MA6000- X% Y2O3 superalloys were characterized by scanning electron microsco...

Full description

Saved in:
Bibliographic Details
Main Authors: Çelik Ş., Özyürek D., Tunçay T.
Format: Article
Language:English
Published: University of Belgrade, Technical Faculty, Bor 2022-01-01
Series:Journal of Mining and Metallurgy. Section B: Metallurgy
Subjects:
Online Access:http://www.doiserbia.nb.rs/img/doi/1450-5339/2022/1450-53392200010C.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
_version_ 1832572831472287744
author Çelik Ş.
Özyürek D.
Tunçay T.
author_facet Çelik Ş.
Özyürek D.
Tunçay T.
author_sort Çelik Ş.
collection DOAJ
description This paper investigated the wear performances of Y2O3 doped MA6000 (Ni-Cr-Al) alloy produced by mechanical alloying (MA). Produced, all powders were pre-formed by cold pressing and sintered in a vacuum environment. Sintered MA6000- X% Y2O3 superalloys were characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD) analysis, density, and hardness measurements. Wear tests of Y2O3 added MA6000 alloys were carried out in a block-on-ring type wear device. In the wear tests, the sliding speed of 1 ms-1 at room temperature (RT) was performed under five different sliding distances (200-1000 m) and three different loads (5 N, 10 N, and 15 N). As a result of the studies, it was determined that the MA-ed MA6000 superalloy powders were homogeneous and flake shape. With the increase amount of Y2O3, hardness of these superalloys increased from 267 to 431 Hv, but the density slightly decreased. Different intermetallic/carbur phases such as Ni3Al and MoC were observed in all compositions. Wear tests show that weight loss and wear rate decreased, and friction coefficient (μ) increased with the increasing amount of Y2O3 additive. Besides, it was determined that as the applied load increased in the wear test, the weight loss increased, but the wear rate and friction coefficient (μ) decreased.
format Article
id doaj-art-b03bf10c7d3041bbabb57501091ca5bd
institution Kabale University
issn 1450-5339
2217-7175
language English
publishDate 2022-01-01
publisher University of Belgrade, Technical Faculty, Bor
record_format Article
series Journal of Mining and Metallurgy. Section B: Metallurgy
spelling doaj-art-b03bf10c7d3041bbabb57501091ca5bd2025-02-02T07:44:44ZengUniversity of Belgrade, Technical Faculty, BorJournal of Mining and Metallurgy. Section B: Metallurgy1450-53392217-71752022-01-0158228529710.2298/JMMB220113010C1450-53392200010CThe effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behaviorÇelik Ş.0Özyürek D.1Tunçay T.2Karabuk University, Faculty of Technology, Department of Manufacturing Engineering, Karabuk, TurkeyKarabuk University, Faculty of Technology, Department of Manufacturing Engineering, Karabuk, TurkeyKarabuk University, Faculty of Technology, Department of Manufacturing Engineering, Karabuk, TurkeyThis paper investigated the wear performances of Y2O3 doped MA6000 (Ni-Cr-Al) alloy produced by mechanical alloying (MA). Produced, all powders were pre-formed by cold pressing and sintered in a vacuum environment. Sintered MA6000- X% Y2O3 superalloys were characterized by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD) analysis, density, and hardness measurements. Wear tests of Y2O3 added MA6000 alloys were carried out in a block-on-ring type wear device. In the wear tests, the sliding speed of 1 ms-1 at room temperature (RT) was performed under five different sliding distances (200-1000 m) and three different loads (5 N, 10 N, and 15 N). As a result of the studies, it was determined that the MA-ed MA6000 superalloy powders were homogeneous and flake shape. With the increase amount of Y2O3, hardness of these superalloys increased from 267 to 431 Hv, but the density slightly decreased. Different intermetallic/carbur phases such as Ni3Al and MoC were observed in all compositions. Wear tests show that weight loss and wear rate decreased, and friction coefficient (μ) increased with the increasing amount of Y2O3 additive. Besides, it was determined that as the applied load increased in the wear test, the weight loss increased, but the wear rate and friction coefficient (μ) decreased.http://www.doiserbia.nb.rs/img/doi/1450-5339/2022/1450-53392200010C.pdfmechanical alloysuperalloyma6000weary2o3
spellingShingle Çelik Ş.
Özyürek D.
Tunçay T.
The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
Journal of Mining and Metallurgy. Section B: Metallurgy
mechanical alloy
superalloy
ma6000
wear
y2o3
title The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
title_full The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
title_fullStr The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
title_full_unstemmed The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
title_short The effect of the amount of Y2O3 doped to the MA6000 alloy produced by mechanical alloying method on wear behavior
title_sort effect of the amount of y2o3 doped to the ma6000 alloy produced by mechanical alloying method on wear behavior
topic mechanical alloy
superalloy
ma6000
wear
y2o3
url http://www.doiserbia.nb.rs/img/doi/1450-5339/2022/1450-53392200010C.pdf
work_keys_str_mv AT celiks theeffectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior
AT ozyurekd theeffectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior
AT tuncayt theeffectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior
AT celiks effectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior
AT ozyurekd effectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior
AT tuncayt effectoftheamountofy2o3dopedtothema6000alloyproducedbymechanicalalloyingmethodonwearbehavior