Optimization of Process Parameters for Vertical-Faced Polypropylene Bottle Injection Molding
In order to obtain the optimal combination of process parameters for vertical-faced polypropylene bottle injection molding, with UG, the model of the bottle was drawn, and then, one module and sixteen-cavity injection molding system was established and analyzed using Moldflow. For filling and mainta...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2018-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2018/2635084 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In order to obtain the optimal combination of process parameters for vertical-faced polypropylene bottle injection molding, with UG, the model of the bottle was drawn, and then, one module and sixteen-cavity injection molding system was established and analyzed using Moldflow. For filling and maintaining pressure during the process of infusion bottle injection molding, the orthogonal test table L25 (56) using CAE was designed for injection molding of the bottle, with six parameters such as melt temperature, mold temperature, injection pressure, injection time, dwell pressure, and dwell time as orthogonal test factors. By finding the best combination of process parameters, the orthogonal experiment was completed, the results were analyzed by range analysis, and the order of influence of each process parameter on each direction of optimization was obtained. The prediction dates of the infusion bottle were gained under various parameters, a comprehensive quality evaluation index of the bottle was formulated, and the multiobjective optimization problem of injection molding process was transformed into a single-objective optimization problem by the integrated weighted score method. The bottle parameters were optimized by analyzing the range date of the weighted scoring method, and the best parameter combination such as melt temperature 200°C, mold temperature 80°C, injection pressure 40 MPa, injection time 2.1 S, dwell pressure 40 MPa, and dwell time 40 S was gained. |
|---|---|
| ISSN: | 1687-8434 1687-8442 |