Improving corrosion and microbial corrosion resistance of CoCrFeNi high entropy alloy in marine environment by trace amount of Ce addition
Microorganisms in marine environments are able to accelerate the local dissolution of passive films formed on high entropy alloy surfaces, significantly reducing the corrosion resistance. The addition of trace amounts of Ce has been reported to modify inclusions, thereby enhancing the pitting resist...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2025-06-01
|
| Series: | Materials & Design |
| Subjects: | |
| Online Access: | http://www.sciencedirect.com/science/article/pii/S0264127525005015 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Microorganisms in marine environments are able to accelerate the local dissolution of passive films formed on high entropy alloy surfaces, significantly reducing the corrosion resistance. The addition of trace amounts of Ce has been reported to modify inclusions, thereby enhancing the pitting resistance of passive films. Herein, the effect of Ce addition in CoCrFeNiCex (x = 0, 0.001, 0.003 and 0.005) HEAs on microbiologically influenced corrosion (MIC) behaviors were investigated in this work. Through Scanning electron microscopy, energy dispersive spectroscopy, electrochemical tests, and X-ray photoelectron spectroscopy (XPS) analysis, we revealed that Ce addition synergistically optimizes inclusion morphology and passive film stability. With the addition of Ce reaching 0.003 in molar ratio, polygonal Al2O3 inclusions in CoCrFeNi HEA were converted into spherical CeAlO3 and the size of inclusions decreased approximately 50 % (1.4 μm), enhancing pitting resistance (Epit = 930 mV). In inoculated medium, CoCrFeNiCe0.003 exhibited shallower pits (0.36 μm) and higher protection potential (Epp = 880 mV), compared to those of CoCrFeNi (0.53 μm and −231 mV). Excessive Ce addition (0.005 in molar ratio) led to the formation of new inclusion, increasing the pitting sensitivity of the alloy. These findings outline a new strategy by inclusions modification to increase the resistance to MIC. |
|---|---|
| ISSN: | 0264-1275 |