Simulated Experiment Study of Factors Influencing the Hydration Activity of f-CaO in Basic Oxygen Furnace Slag
The compositions and formation process of f-CaO in BOF slag were revealed and simulated to understand its expansion rules and why its hydration activity is low. BSE showed the compositions of f-CaO, which included calcium iron phase and calcium iron manganese phase, were diverse. The hydration activ...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2016-01-01
|
| Series: | Advances in Materials Science and Engineering |
| Online Access: | http://dx.doi.org/10.1155/2016/7529382 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The compositions and formation process of f-CaO in BOF slag were revealed and simulated to understand its expansion rules and why its hydration activity is low. BSE showed the compositions of f-CaO, which included calcium iron phase and calcium iron manganese phase, were diverse. The hydration activity sequence was Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; only Ca2Fe2O5 and Ca3Fe1.5Mn1.5O8 were hard to hydrate, and the volume expansion rates of the tricomponent f-CaO varied with different compositions. Inductively, in BOF slag, the hydration activity sequence was solid solutions CaO-FeOx and CaO-FeOx-MnOy in tricomponent f-CaO < CaO in tricomponent f-CaO < monocomponent f-CaO; the volume expansion rates of tricomponent f-CaO changed with different compositions, and CaO-FeOx and CaO-FeOx-MnOy were difficult to hydrate. The reason why solid solutions CaO-FeOx and CaO-FeOx-MnOy were hard to hydrate was that their hydration reaction driving force, which is the absolute value of standard molar reaction Gibbs functions, decreased. |
|---|---|
| ISSN: | 1687-8434 1687-8442 |