Influence of Solution Annealing Temperature on Crystallographic Texture and Grain Disorientation of Nb-Enhanced Maraging Steel: An EBSD Analysis
This study investigates the microstructural and crystallographic changes in a novel Nb-enhanced, Ti-reduced maraging steel. The hot-rolled steel was solution annealed at two different temperatures followed by aging. The Electron Backscatter Diffraction (EBSD) analysis of hot-rolled sample revealed a...
Saved in:
| Main Authors: | , , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
2025-05-01
|
| Series: | Materials Research |
| Subjects: | |
| Online Access: | http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392025000100241&lng=en&tlng=en |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This study investigates the microstructural and crystallographic changes in a novel Nb-enhanced, Ti-reduced maraging steel. The hot-rolled steel was solution annealed at two different temperatures followed by aging. The Electron Backscatter Diffraction (EBSD) analysis of hot-rolled sample revealed a predominant {112}//RP texture, reoriented to {110}//RP during aging to minimize internal energy and stress. Solution annealing at 820oC followed by aging favored a {111} orientation, resulting in minimal crystallographic defects and grain distortion. In contrast, higher solution annealing temperatures promoted the formation of {001} cleavage planes, increasing brittleness and crystal defects, thereby impacting the material's suitability for high-performance applications. |
|---|---|
| ISSN: | 1516-1439 |