Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit
The present study was investigated the effect of fiber mass fraction on the tensile and fatigue strength of oil palm fiber reinforced composite and resin as the matrix. Fatigue test has been performed by using rotary bending fatigue machine. The specimens were made by press hand lay-up with matrix t...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Department of Mechanical Engineering, Faculty of Engineering, Universitas Andalas
2018-12-01
|
| Series: | Metal: Jurnal Sistem Mekanik dan Termal |
| Subjects: | |
| Online Access: | https://metal.ft.unand.ac.id/index.php/metal/article/view/68 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832574963216809984 |
|---|---|
| author | Devi Chandra Randha Mulia Dedison Gasni Gusriwandi Gusriwandi |
| author_facet | Devi Chandra Randha Mulia Dedison Gasni Gusriwandi Gusriwandi |
| author_sort | Devi Chandra |
| collection | DOAJ |
| description | The present study was investigated the effect of fiber mass fraction on the tensile and fatigue strength of oil palm fiber reinforced composite and resin as the matrix. Fatigue test has been performed by using rotary bending fatigue machine. The specimens were made by press hand lay-up with matrix to fiber mass ratio was 90:10, 80:20 and 70:30 respectively. Fracture surface of fatigue specimens have also been observed by using digital camera to knowing the failure mode. The results showed that the tensile and fatigue strength and fatigue life increased with increasing the fiber mass fraction as seen in the S-N curve. The fatigue limit was found 0.27 MPa, 0.55 MPa, and 0.82 MPa for composites with 90:10, 80:20 and 70:30 of matrix to fiber mass ratio respectively. The observed failure modes were matrix cracking, fiber debonding, and fiber breaking. |
| format | Article |
| id | doaj-art-8924c4ad4e474ba58242b0d0aa3fb8ca |
| institution | Kabale University |
| issn | 2598-1137 2597-4483 |
| language | English |
| publishDate | 2018-12-01 |
| publisher | Department of Mechanical Engineering, Faculty of Engineering, Universitas Andalas |
| record_format | Article |
| series | Metal: Jurnal Sistem Mekanik dan Termal |
| spelling | doaj-art-8924c4ad4e474ba58242b0d0aa3fb8ca2025-02-01T10:20:39ZengDepartment of Mechanical Engineering, Faculty of Engineering, Universitas AndalasMetal: Jurnal Sistem Mekanik dan Termal2598-11372597-44832018-12-0122616910.25077/metal.2.2.61-69.201844Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa SawitDevi Chandra0Randha Mulia1Dedison Gasni2Gusriwandi Gusriwandi3Universitas AndalasUniversitas AndalasUniversitas AndalasUniversitas AndalasThe present study was investigated the effect of fiber mass fraction on the tensile and fatigue strength of oil palm fiber reinforced composite and resin as the matrix. Fatigue test has been performed by using rotary bending fatigue machine. The specimens were made by press hand lay-up with matrix to fiber mass ratio was 90:10, 80:20 and 70:30 respectively. Fracture surface of fatigue specimens have also been observed by using digital camera to knowing the failure mode. The results showed that the tensile and fatigue strength and fatigue life increased with increasing the fiber mass fraction as seen in the S-N curve. The fatigue limit was found 0.27 MPa, 0.55 MPa, and 0.82 MPa for composites with 90:10, 80:20 and 70:30 of matrix to fiber mass ratio respectively. The observed failure modes were matrix cracking, fiber debonding, and fiber breaking.https://metal.ft.unand.ac.id/index.php/metal/article/view/68kekuatan fatikmaterial kompositserat sawitfraksi massa |
| spellingShingle | Devi Chandra Randha Mulia Dedison Gasni Gusriwandi Gusriwandi Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit Metal: Jurnal Sistem Mekanik dan Termal kekuatan fatik material komposit serat sawit fraksi massa |
| title | Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit |
| title_full | Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit |
| title_fullStr | Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit |
| title_full_unstemmed | Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit |
| title_short | Pengaruh Fraksi Massa Serat Terhadap Kekuatan Fatik Material Komposit Berpenguat Serat Tandan Kosong Kelapa Sawit |
| title_sort | pengaruh fraksi massa serat terhadap kekuatan fatik material komposit berpenguat serat tandan kosong kelapa sawit |
| topic | kekuatan fatik material komposit serat sawit fraksi massa |
| url | https://metal.ft.unand.ac.id/index.php/metal/article/view/68 |
| work_keys_str_mv | AT devichandra pengaruhfraksimassaseratterhadapkekuatanfatikmaterialkompositberpenguatserattandankosongkelapasawit AT randhamulia pengaruhfraksimassaseratterhadapkekuatanfatikmaterialkompositberpenguatserattandankosongkelapasawit AT dedisongasni pengaruhfraksimassaseratterhadapkekuatanfatikmaterialkompositberpenguatserattandankosongkelapasawit AT gusriwandigusriwandi pengaruhfraksimassaseratterhadapkekuatanfatikmaterialkompositberpenguatserattandankosongkelapasawit |