Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass
Glass that corrodes under natural conditions often shows heterogeneities in the leached layer, such as a lamellar structure or inclusions of MnO2 or Ca3(PO4)2. The formation of these heterogeneities is still not well understood. By means of experiments under laboratory conditions, our aim was to art...
Saved in:
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Association CeROArt
2010-11-01
|
| Series: | CeROArt : Conservation, Exposition, Restauration d'Objets d'Art |
| Subjects: | |
| Online Access: | https://journals.openedition.org/ceroart/1561 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832578106819346432 |
|---|---|
| author | Willemien Anaf |
| author_facet | Willemien Anaf |
| author_sort | Willemien Anaf |
| collection | DOAJ |
| description | Glass that corrodes under natural conditions often shows heterogeneities in the leached layer, such as a lamellar structure or inclusions of MnO2 or Ca3(PO4)2. The formation of these heterogeneities is still not well understood. By means of experiments under laboratory conditions, our aim was to artificially generate specific structures. Therefore, glass samples were immersed in metal-rich solutions. The experimental results were compared with theories describing glass corrosion from a molecular point of view. |
| format | Article |
| id | doaj-art-697a5242b05742928471a039c4237c18 |
| institution | Kabale University |
| issn | 1784-5092 |
| language | English |
| publishDate | 2010-11-01 |
| publisher | Association CeROArt |
| record_format | Article |
| series | CeROArt : Conservation, Exposition, Restauration d'Objets d'Art |
| spelling | doaj-art-697a5242b05742928471a039c4237c182025-01-30T14:13:36ZengAssociation CeROArtCeROArt : Conservation, Exposition, Restauration d'Objets d'Art1784-50922010-11-01110.4000/ceroart.1561Study on the formation of heterogeneous structures in leached layers during the corrosion process of glassWillemien AnafGlass that corrodes under natural conditions often shows heterogeneities in the leached layer, such as a lamellar structure or inclusions of MnO2 or Ca3(PO4)2. The formation of these heterogeneities is still not well understood. By means of experiments under laboratory conditions, our aim was to artificially generate specific structures. Therefore, glass samples were immersed in metal-rich solutions. The experimental results were compared with theories describing glass corrosion from a molecular point of view.https://journals.openedition.org/ceroart/1561Glasscorrosionheterogeneous leached layerpercolation channels |
| spellingShingle | Willemien Anaf Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass CeROArt : Conservation, Exposition, Restauration d'Objets d'Art Glass corrosion heterogeneous leached layer percolation channels |
| title | Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| title_full | Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| title_fullStr | Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| title_full_unstemmed | Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| title_short | Study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| title_sort | study on the formation of heterogeneous structures in leached layers during the corrosion process of glass |
| topic | Glass corrosion heterogeneous leached layer percolation channels |
| url | https://journals.openedition.org/ceroart/1561 |
| work_keys_str_mv | AT willemienanaf studyontheformationofheterogeneousstructuresinleachedlayersduringthecorrosionprocessofglass |