Leaching of hemimorphite in neutral solution at high temperature
The leaching behavior of hemimorphite in neutral solution (NH4 +-Cl--H2O) was investigated at high temperature (T > 100°C) under a range of experimental conditions. Thermodynamic calculations indicate that the tendency of dehydration of silica gel is significantly enhanced with the increasing tem...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
University of Belgrade, Technical Faculty, Bor
2020-01-01
|
| Series: | Journal of Mining and Metallurgy. Section B: Metallurgy |
| Subjects: | |
| Online Access: | http://www.doiserbia.nb.rs/img/doi/1450-5339/2020/1450-53392000014Z.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The leaching behavior of hemimorphite in neutral solution (NH4 +-Cl--H2O) was investigated at high temperature (T > 100°C) under a range of experimental conditions. Thermodynamic calculations indicate that the tendency of dehydration of silica gel is significantly enhanced with the increasing temperature. It was shown that the temperature, ammonium chloride concentration, or L/S ratio increased resulted in greater leaching efficiency. The following optimized leaching conditions were obtained: stirrer speed 400r/min, NH4Cl concentration 5.5M, L/S ratio 9mL/g at 160°C for 3h. Under these optimized conditions, the average leaching yield of zinc was 97.82%. The silicon was converted to quartz and remained in the residue. This process can be used to dispose willemite and hemimorphite as it solves the problem of silica gel dehydration. |
|---|---|
| ISSN: | 1450-5339 2217-7175 |