Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel
100Cr6steel surface was induction hardened in order to be used in a bushingmanufacturing. After examininig themicrostructure and hardness variations of the hardened surfaces, ball-on disctype wear tests were carried out. Weartests were performed at 4,92 mm/s sliding speed, under various loads (2,5-5...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Sakarya University
2018-10-01
|
| Series: | Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi |
| Subjects: | |
| Online Access: | https://dergipark.org.tr/tr/download/article-file/346985 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1850252389649481728 |
|---|---|
| author | Gülcan Toktaş Alaaddin Toktaş Murat Can Duran |
| author_facet | Gülcan Toktaş Alaaddin Toktaş Murat Can Duran |
| author_sort | Gülcan Toktaş |
| collection | DOAJ |
| description | 100Cr6steel surface was induction hardened in order to be used in a bushingmanufacturing. After examininig themicrostructure and hardness variations of the hardened surfaces, ball-on disctype wear tests were carried out. Weartests were performed at 4,92 mm/s sliding speed, under various loads (2,5-5-10N), in dry medium and at room temperature.The results of wear tests were evaluated by the mass loss method. The coefficients of friction were obtainedduring wear tests. The wear tracks andsurfaces were investigated by optic and scanning electron microscopes. Asa result, the surface hardness of the steel was obtained 2,5 times more thanthe core hardness by the aid of formed martensitic matrix structure instead ofpearlitic one on steel surface by induction hardening process. It is seen thatthe highest mass loss was obtained by applying 5 N load in wear tests. |
| format | Article |
| id | doaj-art-41d5e86c23cd4e7bb5e4e28d4c23b0c4 |
| institution | OA Journals |
| issn | 2147-835X |
| language | English |
| publishDate | 2018-10-01 |
| publisher | Sakarya University |
| record_format | Article |
| series | Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi |
| spelling | doaj-art-41d5e86c23cd4e7bb5e4e28d4c23b0c42025-08-20T01:57:40ZengSakarya UniversitySakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi2147-835X2018-10-012251174118010.16984/saufenbilder.30420328Investigating the Wear Behaviour of Induction Hardened 100Cr6 SteelGülcan Toktaş0Alaaddin Toktaş1Murat Can Duran2BALIKESİR ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜBALIKESİR ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜBalıkesir Büyükşehir Belediyesi100Cr6steel surface was induction hardened in order to be used in a bushingmanufacturing. After examininig themicrostructure and hardness variations of the hardened surfaces, ball-on disctype wear tests were carried out. Weartests were performed at 4,92 mm/s sliding speed, under various loads (2,5-5-10N), in dry medium and at room temperature.The results of wear tests were evaluated by the mass loss method. The coefficients of friction were obtainedduring wear tests. The wear tracks andsurfaces were investigated by optic and scanning electron microscopes. Asa result, the surface hardness of the steel was obtained 2,5 times more thanthe core hardness by the aid of formed martensitic matrix structure instead ofpearlitic one on steel surface by induction hardening process. It is seen thatthe highest mass loss was obtained by applying 5 N load in wear tests.https://dergipark.org.tr/tr/download/article-file/346985100cr6 steelinduction hardeningwear |
| spellingShingle | Gülcan Toktaş Alaaddin Toktaş Murat Can Duran Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi 100cr6 steel induction hardening wear |
| title | Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel |
| title_full | Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel |
| title_fullStr | Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel |
| title_full_unstemmed | Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel |
| title_short | Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel |
| title_sort | investigating the wear behaviour of induction hardened 100cr6 steel |
| topic | 100cr6 steel induction hardening wear |
| url | https://dergipark.org.tr/tr/download/article-file/346985 |
| work_keys_str_mv | AT gulcantoktas investigatingthewearbehaviourofinductionhardened100cr6steel AT alaaddintoktas investigatingthewearbehaviourofinductionhardened100cr6steel AT muratcanduran investigatingthewearbehaviourofinductionhardened100cr6steel |