Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates
The effect of scratch damage on the tension properties of carbon fiber plain weave laminates has been studied in detail using digital image correlation (DIC) and acoustic emission (AE). A range of scratch lengths was machined onto different laminates. The bearing capacity of the laminates was then c...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2021-01-01
|
| Series: | Advances in Civil Engineering |
| Online Access: | http://dx.doi.org/10.1155/2021/5590448 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832550057568632832 |
|---|---|
| author | Miaomiao Duan Zhufeng Yue Qianguang Song |
| author_facet | Miaomiao Duan Zhufeng Yue Qianguang Song |
| author_sort | Miaomiao Duan |
| collection | DOAJ |
| description | The effect of scratch damage on the tension properties of carbon fiber plain weave laminates has been studied in detail using digital image correlation (DIC) and acoustic emission (AE). A range of scratch lengths was machined onto different laminates. The bearing capacity of the laminates was then compared with that of unaltered samples. The strain field distributions near the scratches were measured and analyzed as a function of scratch length with DIC. Initiation and propagation of damage were monitored during the tensile tests using AE. Failure sites and morphologies were observed and analyzed. The results show that superficial scratches have little effect on the strength of plain weave laminates when the scratch length is less than 80% of the specimen width. Scratches affect the distribution of strain near the scratch but not far away from the scratch or at the back face of the sample. Not all samples broke from the scratch site but instead broke from the free edge of the sample or close to the gripping region. |
| format | Article |
| id | doaj-art-3dfe4ec08e0e4a849c7cf6054305796a |
| institution | Kabale University |
| issn | 1687-8086 1687-8094 |
| language | English |
| publishDate | 2021-01-01 |
| publisher | Wiley |
| record_format | Article |
| series | Advances in Civil Engineering |
| spelling | doaj-art-3dfe4ec08e0e4a849c7cf6054305796a2025-02-03T06:07:43ZengWileyAdvances in Civil Engineering1687-80861687-80942021-01-01202110.1155/2021/55904485590448Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave LaminatesMiaomiao Duan0Zhufeng Yue1Qianguang Song2School of Mechanics, Civil Engineering and Architecture, Northwestern Polytechnical University, Xi’an 710129, ChinaSchool of Mechanics, Civil Engineering and Architecture, Northwestern Polytechnical University, Xi’an 710129, ChinaBeijing Institute of Structure and Environment Engineering, Beijing 100076, ChinaThe effect of scratch damage on the tension properties of carbon fiber plain weave laminates has been studied in detail using digital image correlation (DIC) and acoustic emission (AE). A range of scratch lengths was machined onto different laminates. The bearing capacity of the laminates was then compared with that of unaltered samples. The strain field distributions near the scratches were measured and analyzed as a function of scratch length with DIC. Initiation and propagation of damage were monitored during the tensile tests using AE. Failure sites and morphologies were observed and analyzed. The results show that superficial scratches have little effect on the strength of plain weave laminates when the scratch length is less than 80% of the specimen width. Scratches affect the distribution of strain near the scratch but not far away from the scratch or at the back face of the sample. Not all samples broke from the scratch site but instead broke from the free edge of the sample or close to the gripping region.http://dx.doi.org/10.1155/2021/5590448 |
| spellingShingle | Miaomiao Duan Zhufeng Yue Qianguang Song Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates Advances in Civil Engineering |
| title | Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates |
| title_full | Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates |
| title_fullStr | Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates |
| title_full_unstemmed | Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates |
| title_short | Effect of Superficial Scratch Damage on Tension Properties of Carbon/Epoxy Plain Weave Laminates |
| title_sort | effect of superficial scratch damage on tension properties of carbon epoxy plain weave laminates |
| url | http://dx.doi.org/10.1155/2021/5590448 |
| work_keys_str_mv | AT miaomiaoduan effectofsuperficialscratchdamageontensionpropertiesofcarbonepoxyplainweavelaminates AT zhufengyue effectofsuperficialscratchdamageontensionpropertiesofcarbonepoxyplainweavelaminates AT qianguangsong effectofsuperficialscratchdamageontensionpropertiesofcarbonepoxyplainweavelaminates |