ITO-Free Semitransparent Organic Solar Cells Based on Silver Thin Film Electrodes
ITO-free semitransparent organic solar cells (OSCs) based on MoO3/Ag anodes with poly(3-hexylthiophene) and [6,6]-phenyl-C61-butyric acid methyl ester films as the active layer are investigated in this work. To obtain the optimal transparent (MoO3)/Ag anode, ITO-free reference OSCs are firstly fabri...
Saved in:
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Wiley
2014-01-01
|
| Series: | International Journal of Photoenergy |
| Online Access: | http://dx.doi.org/10.1155/2014/209206 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | ITO-free semitransparent organic solar cells (OSCs) based on MoO3/Ag anodes with poly(3-hexylthiophene) and [6,6]-phenyl-C61-butyric acid methyl ester films as the active layer are investigated in this work. To obtain the optimal transparent (MoO3)/Ag anode, ITO-free reference OSCs are firstly fabricated. The power conversion efficiency (PCE) of 2.71% is obtained for OSCs based on the optimal MoO3 (2 nm)/Ag (9 nm) anode, comparable to that of ITO-based reference OSCs (PCE of 2.85%). Then based on MoO3 (2 nm)/Ag (9 nm) anode, ITO-free semitransparent OSCs with different thickness combination of Ca and Ag as the cathodes are investigated. It is observed from our results that OSCs with Ca (15 nm)/Ag (15 nm) cathode have the optimal transparency. Meanwhile, the PCE of 1.79% and 0.67% is obtained for illumination from the anode and cathode side, respectively, comparable to that of similar ITO-based semitransparent OSCs (PCE of 1.59% and 0.75% for illumination from the anode and cathode side, resp.) (Sol. Energy Mater. Sol. Cells, 95, pp. 877–880, 2011). The transparency and PCE of ITO-free semitransparent OSCs can be further improved by introducing a light couple layer. The developed method is compatible with various substrates, which is instructive for further research of ITO-free semitransparent OSCs. |
|---|---|
| ISSN: | 1110-662X 1687-529X |