THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE
It is shown that at twisting of wire of diameter 1,83 mm, produced by direct wire drawing of thermomechanically processed rolled wire of diameter 5,5 mm of steel 90, metal stratification is completely eliminated at decrease of carbon, manganese and an additional alloying of chrome.
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Belarusian National Technical University
2011-11-01
|
| Series: | Литьë и металлургия |
| Online Access: | https://lim.bntu.by/jour/article/view/571 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| _version_ | 1832543063102193664 |
|---|---|
| author | V. A. Lutsenko V. G. Chernichenko O. V. Lutsenko I. N. Radjkova V. I. Gritsaenko |
| author_facet | V. A. Lutsenko V. G. Chernichenko O. V. Lutsenko I. N. Radjkova V. I. Gritsaenko |
| author_sort | V. A. Lutsenko |
| collection | DOAJ |
| description | It is shown that at twisting of wire of diameter 1,83 mm, produced by direct wire drawing of thermomechanically processed rolled wire of diameter 5,5 mm of steel 90, metal stratification is completely eliminated at decrease of carbon, manganese and an additional alloying of chrome. |
| format | Article |
| id | doaj-art-0ddd7d5e6d6b4f36838fca177919a797 |
| institution | Kabale University |
| issn | 1683-6065 2414-0406 |
| language | English |
| publishDate | 2011-11-01 |
| publisher | Belarusian National Technical University |
| record_format | Article |
| series | Литьë и металлургия |
| spelling | doaj-art-0ddd7d5e6d6b4f36838fca177919a7972025-02-03T11:52:23ZengBelarusian National Technical UniversityЛитьë и металлургия1683-60652414-04062011-11-0104102104565THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIREV. A. Lutsenko0V. G. Chernichenko1O. V. Lutsenko2I. N. Radjkova3V. I. Gritsaenko4Iron and Steel Institute of NAS UkraineIron and Steel Institute of NAS UkraineIron and Steel Institute of NAS UkraineByelorussian Steel WorksByelorussian Steel WorksIt is shown that at twisting of wire of diameter 1,83 mm, produced by direct wire drawing of thermomechanically processed rolled wire of diameter 5,5 mm of steel 90, metal stratification is completely eliminated at decrease of carbon, manganese and an additional alloying of chrome.https://lim.bntu.by/jour/article/view/571 |
| spellingShingle | V. A. Lutsenko V. G. Chernichenko O. V. Lutsenko I. N. Radjkova V. I. Gritsaenko THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE Литьë и металлургия |
| title | THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE |
| title_full | THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE |
| title_fullStr | THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE |
| title_full_unstemmed | THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE |
| title_short | THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE |
| title_sort | thermo mechanically processed rolled wire for high strength on board wire |
| url | https://lim.bntu.by/jour/article/view/571 |
| work_keys_str_mv | AT valutsenko thermomechanicallyprocessedrolledwireforhighstrengthonboardwire AT vgchernichenko thermomechanicallyprocessedrolledwireforhighstrengthonboardwire AT ovlutsenko thermomechanicallyprocessedrolledwireforhighstrengthonboardwire AT inradjkova thermomechanicallyprocessedrolledwireforhighstrengthonboardwire AT vigritsaenko thermomechanicallyprocessedrolledwireforhighstrengthonboardwire |